Taisn 102 Casting Defect Rebuilding Epoxy Putty
Product Description:
Double components, fluid type. Used for repairing and restoring blowholes, shrinkage, flow marks and
cracks in castings with defect size up to 2mm.
Physical Properties:
Color: | Grey |
Specific gravity: | 1.43g/cm³ |
Mix ratio by weight: | 2:1 |
Mix ratio by volume: | 2:1 |
Working time(min): | 60min |
Compressive strength(GB/T1041): | 95.0MPa |
Tensile strength(GB/T6329): | 35.0MPa |
Shear strength(GB/T7124): | 20.0MPa |
Flexural strength(GB/T9341): | 67.0MPa |
Hardness(GB/T2411): | 80Shore D |
Cured time for machining: | 18h |
Temperature range: | -60~120℃ |
Packing:
500g/set, 5kg/set, 10kg/set or customize
Attention
1、When the temperature is below 15 ℃, some heating measures should be adopted; or the relevant curing time should be extended
2、When mix volume is more than 200g, the working time will be shorter
3、Above data is typical
Taisn 102 Casting Defect Rebuilding Epoxy Putty
Product Description:
Double components, fluid type. Used for repairing and restoring blowholes, shrinkage, flow marks and
cracks in castings with defect size up to 2mm.
Physical Properties:
Color: | Grey |
Specific gravity: | 1.43g/cm³ |
Mix ratio by weight: | 2:1 |
Mix ratio by volume: | 2:1 |
Working time(min): | 60min |
Compressive strength(GB/T1041): | 95.0MPa |
Tensile strength(GB/T6329): | 35.0MPa |
Shear strength(GB/T7124): | 20.0MPa |
Flexural strength(GB/T9341): | 67.0MPa |
Hardness(GB/T2411): | 80Shore D |
Cured time for machining: | 18h |
Temperature range: | -60~120℃ |
Packing:
500g/set, 5kg/set, 10kg/set or customize
Attention
1、When the temperature is below 15 ℃, some heating measures should be adopted; or the relevant curing time should be extended
2、When mix volume is more than 200g, the working time will be shorter
3、Above data is typical