Taisn 114 Copper-filled Epoxy Putty
Product Description:
Double components, copper-filled epoxy putty. Suitable for rebuilding copper bushings, shafts, castings and defected parts.
Technical Data Sheet:
Color: | Brass |
Specific gravity: | 1.53g/cm³ |
Mix ratio by weight: | 6:1 |
Mix ratio by volume: | 4:1 |
Working time(min): | 80min |
Compressive strength(GB/T1041): | 100.0MPa |
Tensile strength(GB/T6329): | 40.0MPa |
Shear strength(GB/T7124): | 21.0MPa |
Flexural strength(GB/T9341): | 56.0MPa |
Hardness(GB/T2411): | 81Shore D |
Curing time before processing or loading: | 24h |
Temperature range: | -60~160℃ |
Packing:
500g/set, 5kg/set, 10kg/set or customize
Attention
1、When the temperature is below 15 ℃, some heating measures should be adopted; or the relevant curing time should be extended
2、When mix volume is more than 200g, the working time will be shorter
3、Above data is typical
Taisn 114 Copper-filled Epoxy Putty
Product Description:
Double components, copper-filled epoxy putty. Suitable for rebuilding copper bushings, shafts, castings and defected parts.
Technical Data Sheet:
Color: | Brass |
Specific gravity: | 1.53g/cm³ |
Mix ratio by weight: | 6:1 |
Mix ratio by volume: | 4:1 |
Working time(min): | 80min |
Compressive strength(GB/T1041): | 100.0MPa |
Tensile strength(GB/T6329): | 40.0MPa |
Shear strength(GB/T7124): | 21.0MPa |
Flexural strength(GB/T9341): | 56.0MPa |
Hardness(GB/T2411): | 81Shore D |
Curing time before processing or loading: | 24h |
Temperature range: | -60~160℃ |
Packing:
500g/set, 5kg/set, 10kg/set or customize
Attention
1、When the temperature is below 15 ℃, some heating measures should be adopted; or the relevant curing time should be extended
2、When mix volume is more than 200g, the working time will be shorter
3、Above data is typical