TS2000 Type Conveyor Belt Bonding Adhesive, Can Repalce Tiptop SC2000 Cold Bond Cement
Product Description:
TS2000 is cold vulcanized splicing cement. Double components, high strength, good flexibility adhesive. Applied for self-adhesion or bonding between conveyor, rubber, fabric, leather. Peeling strength at bonding area is higher than combination strength between rubber and fabric. 1000g/set, 10sets/carton.
How to use:
1, Surface treatment: Deburring the parts to be bonded. Clean and dry the parts.
2, Mix: Pour the B-part into A-part directly and stir them quickly. Then, pour the mixed adhesive to the parts.
3, Curing: Curing time is 2 hours at room temperature. After 24 hours, it can get to highest bonding strength.
Technical data sheet:
| Part No. | Color | Appearance | Density(g/cm³) | Peel strength(N/cm) GB/T2791-1995 | Mix ratio | Operating time(min) | Curing time | Heat resistant(°C) |
| TS2000 | Black | Liquid | 0.9-1.3 | 110 | A:B=100:4 | 20-40 | 2 hours | 100 |
Packing:
1kg/set, 10sets/carton;
TS2000 Type Conveyor Belt Bonding Adhesive, Can Repalce Tiptop SC2000 Cold Bond Cement
Product Description:
TS2000 is cold vulcanized splicing cement. Double components, high strength, good flexibility adhesive. Applied for self-adhesion or bonding between conveyor, rubber, fabric, leather. Peeling strength at bonding area is higher than combination strength between rubber and fabric. 1000g/set, 10sets/carton.
How to use:
1, Surface treatment: Deburring the parts to be bonded. Clean and dry the parts.
2, Mix: Pour the B-part into A-part directly and stir them quickly. Then, pour the mixed adhesive to the parts.
3, Curing: Curing time is 2 hours at room temperature. After 24 hours, it can get to highest bonding strength.
Technical data sheet:
| Part No. | Color | Appearance | Density(g/cm³) | Peel strength(N/cm) GB/T2791-1995 | Mix ratio | Operating time(min) | Curing time | Heat resistant(°C) |
| TS2000 | Black | Liquid | 0.9-1.3 | 110 | A:B=100:4 | 20-40 | 2 hours | 100 |
Packing:
1kg/set, 10sets/carton;